Pump casing

Pump casing


The pump casing we offer can meet the followings: 

1.  Tolerance size of the casting shall conform to ISO8026-3 DCTG 13-RMA 6(RMAG H)-GCTG 7-DS 

2.  Cracks, burnt, sand and slag inclusions are not allowed. On the unhandled surfaces should not be defects reducing the strength, performance and degrade casting presentation. Allowed correction of welding, in which defective cutting may be performed by the manufacturer's instruction. Locations of these defects in the casting and the butchering size under welding must be registered and entered in the casting documents. After removal of butchering defects, the surface should be grinded and monitored for completeness remove defects by dye penetration 

3. Carry out UT of the castings: the end surfaces along the entire length in the area of the flange connector of the pump housing and cover (zone 1) in the area of the suction flange connector (zone2),in the area of the discharge flange connector (zone3), permitted without correcting defects of the equivalent size to 5mm not more than 3pcs.

4. The conformity checking with the chemical composition of the steels should be carried out from the each melt.


Our main material for cast iron pump cases is similar to followings:


                                                       Standard Specifications for Cast Iron

Country                                                                Standard                                                       Grade

China                                                                   GB 9439                                                        HT150,HT200

United Kingdom                                                    BS 1452                                                        Grade150

USA                                                                      ASTM   A 48                                                  20B

                                                                             ASTM   A159                                                 G1800

Germany                                                              DIN 1691                                                        GG15, GG20

Europe                                                                 EN1563                                                          GJL150,GJL200

Japan                                                                   JIS G5501                                                       FC150,FC200

International                                                         ISO 185                                                          150,200


5. The steel mechanical properties: Tensile strength not less 441MPa, elongation Q not less 19%, impact strength not less 392KJ/m2, hardness HB 121-151. The mechanical properties of the steel are necessary to control for each melt. Test results apply to all the castings from this melt, heat-treated in the same mode, record by automatic devices.


Production Process  

1. Wooden pattern Production  

2. Molding 

3. Pouring 

4. First cleaning 

5. Heat treatment – grinding (inspection)

6. Rough machining (inspection)-finishing machining (inspection)

7. Packing-delivering


Quality assurance 

The fabrication route is governed by the provisions of the implemented Quality System ISO 9001: 2000. The standard documentation ensures the full traceability of every process step: 

• Manufacturer test certificates according to DIN EN 10.204 § 3.1 including chemical composition, mechanical properties and non-destructive examination; 

• Dimensional check supported with a “as-built“ sketch; 

• Record of the heat treatment chart